What is aluminum 6061-T6 used for?
6061 Aluminum Sheet The T6 refers to the temper or degree of hardness, which is achieved by precipitation hardening. This grade has a good strength-to-weight ratio and is also heat-treatable. With great formability and weldability, it is used for engineering and structural applications, boats, furniture, and more.
What is T6 condition for aluminum?
The T6 temper designation means that the aluminum alloy has been given a solution heat treatment followed by quenching, cooling, and aging. Artificially aging allows the material to achieve the desired precipitation hardening.
What type of metal alloy is aluminum 6061-T6?
Aluminium alloy 6061 is a medium to high strength heat-treatable alloy with a strength higher than 6005A. It has very good corrosion resistance and very good weldability although reduced strength in the weld zone. It has medium fatigue strength.
What is the difference between 6061 T4 and 6061 T6?
Generally, 6061 aluminum is solution heat treated, then aged. T4 temper aluminum is naturally aged, and T6 temper aluminum is artificially aged for maximum strength.
How hard is 6061-T6 aluminum?
T6 temper 6061 has an ultimate tensile strength of at least 42,000 psi (290 MPa) and yield strength of at least 35,000 psi (241 MPa).
How strong is 6061 aluminum alloy?
6061-T6. T6 temper 6061 has an ultimate tensile strength of at least 42,000 psi (290 MPa) and yield strength of at least 35,000 psi (241 MPa). In thicknesses of 0.250 inch (6.35 mm) or less, it has elongation of 8% or more; in thicker sections, it has elongation of 10%.
How can you tell 6061 from 6063?
When compared to 6061 AL, 6063 aluminum has a higher melting temperature, higher thermal conductivity, and higher heat capacity. AL 6063 has a better surface finish than AL 6061 and is preferrable for architectural purposes.
Is it possible to bend 6061 T6 aluminum?
Answer: 6061-T6 aluminum is tempered and notorious for not bending easily. From a bending perspective, it’s always best to bend these parts in an annealed state and then temper them to the correct condition. That’s the ideal, anyway, but the reality is that many parts arrive at the press brake in a less than ideal state.
What kind of alloy is Al 6061 T6?
The temper designations mainly have 6061-T4, T451, AL 6061-T6, 6061-T651, etc. It is one of the most widely used alloys. The main alloying elements are magnesium (Mg) and silicon (Si). The content of silicon and magnesium in this alloy is close to form magnesium silicide (Mg2Si), so it is a heat-treated wrought alloy.
What does T6511 stand for in 6061 aluminum?
For instance, -T6511 would indicate that the alloy was solution heat-treated, stress-relieved by stretching, and artificially aged to reduce the possibility of distortion in machined parts. The common grades of commercial 6061 aluminum are 6061-0, 6061-T4, and 6061-T6; however, tempers up to -T9 are produced.
What does T6 stand for in aluminum alloy?
The alpha-numeric suffixes attached to alloys, such as 6061-T6, represent the temper, or degree of hardness. They also represent the method by which the hardness was obtained. In the case of 6061-T6 aluminum alloy, the “T6” indicates that it was solution heat-treated and artificially aged.