What is weldox steel?
Weldox/Strenx is the brand name of hot-rolled sheet steel from SSAB. This high-strength steel is low-alloy, cold-formed steel intended for use in the automotive and engineering industries.
What is weldox 700?
Weldox 700 is a general structural steel with a minimum yield strength of 650 – 700 MPa depending on thickness. Weldox 700 meets the requirements of EN 10025 for the corresponding grades and thicknesses. Typical applications are demanding load- bearing structures.
What Strenx 700?
Strenx® 700 CR is a cold-rolled structural steel with a minimum yield strength of 700 MPa used to produce stronger and lighter structures. Strenx® 700 CR comes in cut-to-length sheets. Typical applications include a wide range of components and parts, for example load-bearing structures.
What is Strenx steel?
Strenx®/Domex® 100XF steel is a thermostatically rolled sheet, 100% iron ore-based product with a minimum yield strength of 100ksi. It is also ideal in applications where improved strength and weight reduction is desired due to its higher yield strength over normally used 50ksi minimum yield strength grades.
What is weldox 900?
WELDOX 900 is a general structural steel with a minimum yield strength of 900 N/mm2 intended for applications where its high strengh permits weight savings to be made. The plate has very good cold bending properties and very good weldability.
What is hardox plate?
Hardox® wear plate is the world’s leading abrasion-resistant (AR) steel. Hardox® is hard through and through, from the surface deep. down to its core, giving you extended service life and high productivity in the most challenging environments.
What is Strenx?
Domex/Strenx is the brand name of hot-rolled sheet steel from SSAB. This high-strength steel is a low-alloy, cold-formed steel intended for use in the automotive and engineering industries. This high-strength steel has excellent formability, and good weldability meaning it can undergo various manufacturing processes.
What is s690 grade steel?
S690QL is a high strength quenched and tempered steel grade that complies to steel specification EN 10025. The designation S690QL refers to a minimum yield strength of 690 MPa.
What is hardox 500?
Hardox® 500 is a bendable and weldable abrasion-resistant steel, with a nominal hardness of 500 HBW. Suitable for applications that demand higher wear resistance. Hardox® 500 increases payload and increases service life while maintaining good processability and toughness.
Is Hardox brittle?
The scatter is caused by large inclusion particles that are found in Hardox-400 steel. Although their percentage content is low, they can cause brittle fracture if they are located in front of the crack tip, where the maximum level of the opening stress is found [14].
Is Hardox a carbon steel?
Hardox® 400 is an abrasion-resistant steel with a nominal hardness of 400 HBW. Hardox® 400 is an all-around wear resistant steel. Thanks to its high toughness, good bendability and weldability, this steel can be used in structures with moderate wear.
Is Domex high carbon steel?
Domex 700 has been rebranded in 2015 as Strenx. Domex/Strenx is the brand name of hot-rolled sheet steel from SSAB. This high-strength steel is a low-alloy, cold-formed steel intended for use in the automotive and engineering industries.
What is the yield strength of weldox 700?
Weldox 700 is a general structural steel with a minimum yield strength of 700 MPa. Weldox 700 meets the requirements for the corresponding steel grades and qualities according to EN 10025.Weldox 700 is a high strength structural steel (700 MPa) with outstanding toughness for a multitude of load carrying structures and other applications.
What is the yield strength of Strenx 700 E / F?
Strenx® 700 E/F is a structural steel with a minimum yield strength of 650-700 MPa depending on thickness. Strenx ® 700 E/F meets the requirements of EN 10 025-6 for the S690 grade and thicknesses. Typical applications include demanding load-bearing structures.
How big is a Strenx 700 E plate?
Strenx ® 700 E (complies with S690QL) is available in plate thicknesses of 4–160 mm, while Strenx® 700 F (complies with S690QL1) is available in plate thicknesses of 4–130 mm. Strenx ® 700 E is available as plate in thicknesses of 4.0 – 160.0 mm and Strenx ® 700 F is available as plate in thicknesses of 4.0 – 130.0 mm.
Which is the best welding method for Strenx 700?
Strenx ® 700 can be welded using any conventional welding method. MAG welding is the most common technique today, since it is very easy to automate for high productivity. Strenx ® 700 can usually be machined without special equipment.